AbstractCyclic oxidation and hot corrosion behaviours of aluminide and Si modified aluminide diffusion coatings deposited on two superalloys are compared in the paper. Samples based on cast nickel superalloys with and without protective coatings were studied under cyclic oxidation and hot corrosion conditions. The main goal of the paper was to compare the cyclic oxidation and hot corrosion resistance of protective aluminide coatings deposited on two types of nickel superalloys, Inconel 713LC and MAR-M247. All samples were exposed to cyclic oxidation and hot corrosion environment at Silesian University of Technology in Katowice, Poland. Hitachi SEM with EDS microanalysis was used for analysis of surfaces and cross-sections of the samples. Ex...
The hot corrosion behavior of the B2 nickel aluminides was studied to determine the inherent hot cor...
International audienceThe respective influence of the oxidation and phase transformation on the rump...
Oxidation behavior of the uncoated base, Ni–Al coated and Re–Cr-Ni plus Ni–Al coated single-crystal ...
AbstractCyclic oxidation and hot corrosion behaviours of aluminide and Si modified aluminide diffusi...
The diffusion aluminide coatings are used for high-temperature applications. Structural materials of...
This thesis reports on investigations of high temperature oxidation resistant aluminide diffusion co...
With increasing challenges from energy and climate, it is critical to reduce the emission of greenho...
The nickel aluminides are commonly employed as a bond coat material in thermal barrier coating syste...
International audienceProtective coatings are used on gas turbine components to enable them to survi...
Pt-, Pd-, and Pt/Pd-modified aluminide coatings were prepared on Inconel 738LC by pack aluminizing a...
Diffusion aluminide coatings are widely employed to increase oxidation resistance of superalloy comp...
The study aims to investigate the effect of Al2O3 and Al additions to Nickel-base superalloys as a c...
High temperature oxidation and corrosion of Ni-based superalloys used for blades in industrial gas t...
Materials used for high temperature applications works in a very aggressive environment (oxidation, ...
AbstractFour modified Al diffusion coatings (Al, Cr–Al, Al–Si and Cr–Al–Si coatings) were prepared o...
The hot corrosion behavior of the B2 nickel aluminides was studied to determine the inherent hot cor...
International audienceThe respective influence of the oxidation and phase transformation on the rump...
Oxidation behavior of the uncoated base, Ni–Al coated and Re–Cr-Ni plus Ni–Al coated single-crystal ...
AbstractCyclic oxidation and hot corrosion behaviours of aluminide and Si modified aluminide diffusi...
The diffusion aluminide coatings are used for high-temperature applications. Structural materials of...
This thesis reports on investigations of high temperature oxidation resistant aluminide diffusion co...
With increasing challenges from energy and climate, it is critical to reduce the emission of greenho...
The nickel aluminides are commonly employed as a bond coat material in thermal barrier coating syste...
International audienceProtective coatings are used on gas turbine components to enable them to survi...
Pt-, Pd-, and Pt/Pd-modified aluminide coatings were prepared on Inconel 738LC by pack aluminizing a...
Diffusion aluminide coatings are widely employed to increase oxidation resistance of superalloy comp...
The study aims to investigate the effect of Al2O3 and Al additions to Nickel-base superalloys as a c...
High temperature oxidation and corrosion of Ni-based superalloys used for blades in industrial gas t...
Materials used for high temperature applications works in a very aggressive environment (oxidation, ...
AbstractFour modified Al diffusion coatings (Al, Cr–Al, Al–Si and Cr–Al–Si coatings) were prepared o...
The hot corrosion behavior of the B2 nickel aluminides was studied to determine the inherent hot cor...
International audienceThe respective influence of the oxidation and phase transformation on the rump...
Oxidation behavior of the uncoated base, Ni–Al coated and Re–Cr-Ni plus Ni–Al coated single-crystal ...