Oxide particle coarsening at temperature over 1473K in 9CrODS steel

AbstractThe oxide particle coarsening was evaluated at temperature over 1473K by means of transmission electron microscopy (TEM). After annealing of the 9CrODS extruded bar, the size of oxide particles increases while the number density decreases, indicating that the oxide particles coarsen through Ostwald ripening. The growth rate of the oxide particles follows the fifth-power law, which is in the region of dislocation ‘pipe’ diffusion. The activation energy for pipe diffusion, however, was remarkably high, derived as 891KJ/mole. The stability of oxide particles and the difference of the diffusion velocity in between bcc-δ phase and fcc-γ phase should be considered as the contributions to the activation energy