Dry Methane Reforming Performance of Ni-based Catalyst Coated onto Stainless Steel Substrate

AbstractIn this work, the Ni-based catalysts (10wt.%Ni/Al2O3-MgO and 10wt.%Ni/MgO) were synthesized by sol-gel method. Each catalyst was prepared as catalyst pellets and catalyst-coated plate, stainless steel plate coated with catalyst. The catalyst-coated plates were fabricated using spray coating. The dry methane reforming (DMR) performances of catalyst-coated plate were investigated and compared with DMR performances of catalyst pellets. As the mass transfer was improved, the methane consumption rate per gram of catalyst coated onto metal plate was ten times greater than those of catalyst pellets approximately. The carbon deposition was also significantly prevented when the catalyst was constructed as a thin-film layer on the plate under our developing condition. Therefore, this catalyst-coated plate can be further developed for multichannel reactor