Photoluminescence properties of europium doped di-strontium magnesium di-silicate phosphor by solid state reaction method

AbstractEuropium doped di-strontium magnesium di-silicate phosphor namely (Sr2MgSi2O7:Eu3+) was prepared by the traditional high temperature solid state reaction method. The phase structure of sintered phosphor was akermanite type structure which belongs to the tetragonal crystallography with space group P42¯1m, this structure is a member of the melilite group and forms a layered compound. The EDX and FTIR spectra confirm the present elements in Sr2MgSi2O7:Eu3+ phosphor. Photoluminescence measurements showed that the phosphor exhibited strong emission peak with good intensity, corresponding to 5D0 → 7F2 (613 nm) red emission and weak 5D0 → 7F1 (590 nm) orange emission. The excitation spectra monitored at 613 nm show broad band from 220 to 300 nm ascribed to O–Eu charge-transfer band (CTB) centered at about 269 nm, and the other peaks in the range of 300–400 nm originated from f–f transitions of Eu3+ ions. The strongest band at 395 nm can be assigned to 7F0 / 5L6 transition of Eu3+ ions due to the typical f–f transitions within Eu3+ of 4f6 configuration