Electronic behaviour of Au-Pt alloys and the 4f binding energy shift anomaly in Au bimetallics- X-ray spectroscopy studies

The electronic structure and charge redistribution of 6s conduction charge and 5d charge in Au and Pt alloys, Au9Pt and AuPt9 have been investigated using a charge compensation model. It is found that, both the Au and Pt 4f binding energy (BE) exhibits a negative shift in the alloys relatively to the pure metal in apparent disagreement with electroneutrality considerations (Au is the most electronegative metallic element); more interestingly, the negative Au 4f BE shift in Au-Pt alloy is in contrast to previous observations for a large number of Au bimetallic systems with more electropositive hosts in which the more electropositive the host„ the more positive the Au 4f BE shift. This anomaly is counter intuitive to electronegativity considerations. This dilemma was resolved by the charge compensation model in which both electronegativity and charge neutrality can be satisfied and the overall charge flow δ, onto Au is small and positive and δ arises from charge flow of 6s conduction charge, Δnc onto Au site, which is partially compensated by the depletion of 6d charge Δnd at the Au site (δ = Δnc+ Δnd ∼0.1 >0). The much larger Coulomb interaction between 4f and 5d than that between 4f and 6s results in positive 4f BE shifts. The Au 4f BE shift in Au-Pt alloys together with 193Au Mössbauer data were used in the charge compensation model analysis which shows that the model is still valid in that the Au 4f shift in Au-Pt alloy arises from mainly conduction charge gain with little depletion of d charge at the Au site. The model also works for Pt. The Au and Pt 5d character in the alloys have been examined with valence band spectra which show both maintain their d characteristic in dilute alloys with Pt d piling up at the Fermi level, and the top of the Au valence band being pushed toward the Fermi level; this is confirmed with DFT densities of state calculations. When Pt is diluted in Au, it gains d charge as evident from the reduction in whiteline intensity at the Pt L3-edge XANES. What emerges from this work is a picture in which the s-d charge compensation in Au bimetallic alloys is triggered by electronegativity difference between Au and the host. For Au-Pt and Au-Pd systems, the difference in electronegativity is very small, conduction charge transfer dominates, and the Au 4f shift is negative whereas in most Au bimetallics, the larger the electronegativity difference, the larger the compensation and the larger the Au 4f shifts