Optimization of A354 Al-Si-Cu-Mg Alloy Heat Treatment: Effect on Microstructure, Hardness, and Tensile Properties of Peak Aged and Overaged Alloy

The aim of the present work is the study of T6 heat treatment of A354 (Al-Si-Cu-Mg) casting alloy. The heat treatment was optimized by maximizing mechanical strength of the alloy while keeping the treatment cost effective, reducing treatment time and temperature. Due to the presence of low melting compounds, a double stage solution treatment was proposed. The first stage was aimed at the homogenization and dissolution of the low melting phase while a second stage at a higher temperature was evaluated to foster dissolution of Cu/Mg rich intermetallics and keep the solution time and temperature as low as possible. Microstructural investigations were performed through optical and electronic microscopy, which allowed the assessment of the evolution of intermetallic phases during the solution treatment. Artificial aging was studied at different temperatures from 160 °C to 210 °C where the peak aging condition was identified. Over aging of the heat treated alloy was evaluated by soaking T6 samples at 200, 245, and 290 °C for up to 168 h. Tensile behavior of the T6 and over-aged alloy (i.e., after soaking at 210 °C for 50 h) was evaluated at room temperature. Results showed that the proposed treatment allowed the enhancement of mechanical properties of the alloy in comparison to industrial practice treatment, maintaining a good level of ductility and conferring a superior resistance to long-term high temperature exposure