Shear Bond Strength of Self-Adhesive Flowable Composite, Conventional Flowable Composite and Resin-Modified Glass Ionomer Cement to Primary Dentin

Objectives: This study aimed to compare the shear bond strength (SBS) of self-adhesive and conventional flowable composites and resin-modified glass-ionomer cement (RMGIC) to primary dentin. Materials and Methods: In this in vitro, experimental study, the buccal surface of 48 primary canine and first molar teeth was longitudinally sectioned to expose dentin. The teeth were randomly divided into three groups (n=16) of 37.5% phosphoric acid+ OptiBond+ Premise Flow composite (group 1), Vertise Flow composite (group 2) and RMGIC (group 3). A plastic cylindrical mold was placed on the exposed dentin and filled with restorative materials. The samples were then immersed in distilled water at 37°C for 24 hours, subjected to 1000 thermal cycles between 5-55°C and underwent SBS test. Mode of failure was determined under a stereomicroscope. Data were analyzed using one-way ANOVA and Tukey’s test. Results: A significant difference was noted in SBS of the groups (P0.05). Failure at the dentin-restoration interface (adhesive failure) had the highest frequency in groups 1 and 2. The frequency of adhesive failure was 100% in group 3. Conclusion: Conventional flowable composite yielded the highest SBS. Considering the advantages of self-adhesive flowable composite such as decreased chair time, easy clinical application and comparable SBS to that of RMGIC, it can serve as an alternative to RMGIC for restoration of primary teeth in uncooperative children