Effect of holding time, thickness and heat treatment on microstructure and mechanical properties of compacted graphite cast iron

The effect of holding time, thickness and annealing heat treatment on the microstructure and some mechanical properties of compacted graphite iron (CGI) are studied. Samples of CGI are produced in Helwan factory for casting by using GGG 70 as base metal in a medium frequency induction furnace. The mechanical properties (tensile strength, and hardness) of the as-cast and after heat treatment samples are determined and the microstructure of the samples is examined using optical microscope. The results show that the mechanical properties and microstructure of CGI depend on holding time, thickness and annealing heat treatment; it is found that increasing the holding time from 10 min to 17 min results in lowering the Mg content from 0.031% to 0.021% and as a result lower nodularity was obtained. Lowering the thickness from 20 mm to 5 mm increases the tendency of dendritic structure as a result of increasing the cooling rate. The annealed samples with mainly ferritic matrix gave the lowest tensile strength and hardness value compared with the as-cast conditions. Keywords: Compacted graphite iron (CGI), Heat treatment, Microstructures, Mechanical propertie