Effects of Thermal Aging on the Low Cycle Fatigue Behaviors of Cast Duplex Stainless Steels

The low cycle fatigue (LCF) behaviors of cast duplex stainless steel (CDSS) thermally aged at different times were investigated under different strain amplitudes. The effects of thermal aging on the LCF lives of CDSS are closely related to the strain amplitude. At a low strain amplitude, the fatigue life of the material increases significantly after thermal aging, while the LCF life decreases with an increasing aging time at a high strain amplitude. After thermal aging at 400 °C for 10,000 h, the fatigue fracture morphologies of CDSS change from fatigue fringes to mixture features including fatigue fringes in austenite and cleavage cracks in ferrite. Severe plastic deformation in ferrite of the aged CDSS under a high strain amplitude causes the cleavage cracking of ferrite. The premature failure of ferrite accelerates the propagation of fatigue crack and shortens the fatigue life at a high strain amplitude