Investigation on the Slag-Steel Reaction of Mold Fluxes Used for Casting Al-TRIP Steel

The reaction between [Al] in molten steel and (SiO2) in the liquid slag layer was one of the restrictive factors in the quality control for high Al-TRIP steel continuous casting. In this work, the composition and property variations of two slags during a slag-steel reaction were analyzed. Accordingly, the crystalline morphologies of slag were discussed and the solid layer lubrication performance was evaluated by Jackson α factors. In addition, a simple kinetics equilibrium model was established to analyze the factors which affected SiO2 consumption. The results reflected that slag-steel reacted rapidly in the first 20 minutes, resulting in the variation of viscosity and the melting temperature of slags. The slag-steel reaction also affected the crystal morphology significantly. Slag was precipitated as crystals with a higher melting temperature, a higher Jackson α factor, and a rougher boundary with the consumption of SiO2 and the generation of Al2O3. In other words, although generated Al2O3 acted as a network modifier to decrease the viscosity of the liquid slag layer adjacent slab shell, the consumption of SiO2 led to the deterioration of the lubrication performance in the solid slag layer adjacent copper, which was detrimental to the quality control for high Al-TRIP steel. Finally, a kinetics equilibrium model indicated that it is possible to reduce a slag-steel reaction by adjusting factors, such as the diffusion coefficient k, c SiO 2 , ρ f and L f , during the actual continuous casting process