Self-Assembly of Stimuli-Responsive Biohybrid Synthetic‑<i>b</i>‑Recombinant Block Copolypeptides

The synthesis and original thermoresponsive behavior of hybrid diblock copolypeptides composed of synthetic and recombinant polypeptides are herein reported. A thermoresponsive recombinant elastin-like polypeptide was used as a macroinitiator to synthesize a range of poly­(l-glutamic acid)-block-elastin-like polypeptide (PGlu-b-ELP) diblock copolypeptides with variable PGlu block lengths. Their temperature-triggered self-assembly in water and in phosphate-buffered saline (PBS) was investigated at the macroscopic scale using complementary techniques such as turbidimetry, dynamic and static light scattering, small-angle neutron scattering, and at the molecular scale by 1H NMR and circular dichroism (CD). In deionized water, PGlu-b-ELP copolypeptides showed one transition from free soluble chains below the transition temperature (Tt) of the ELP block to macroscopic aggregates above the Tt. In contrast, in PBS, four successive regimes were observed upon increasing temperature: below the Tt, copolypeptides were soluble, above the Tt, large aggregates appeared and fell apart into discrete and defined spherical nanoparticles at a temperature named critical micellization temperature (CMT), before finally reaching an equilibrium. During the last regime, neutron scattering experiments revealed that the micelle-like structures underwent a densification step and expelled water from their core. In addition, 1H NMR and CD experiments revealed, in deionized water, the formation of type II β-turns into the ELP block upon temperature increase. These β-turns are known to participate in the intrinsic thermoresponsive behavior of the ELPs. In contrast, in PBS, circular dichroism measurements showed an attenuation of folded structure during the self-assembly phase, leading to less cohesive aggregates able to reorganize into nanoparticles at the CMT