Molecular Orientation Change in Naphthalene Diimide Thin Films Induced by Removal of Thermally Cleavable Substituents

The potential of naphthalene-1,8:4,5-tetracarboxylic diimide (NDI-H) as a transparent electron-transporting material was examined. A soluble precursor was designed and synthesized having two tert-butoxycarbonyl solubilizing substituents at the imide moieties. This precursor molecule, NDI-Boc, is converted to the hydrogen-substituted NDI-H by heating the spin-coated precursor films. The molecular orientation during the thermal conversion of NDI-Boc to NDI-H was examined using two-dimensional grazing incidence X-ray diffraction (2D-GIXD) and p-polarized multiple-angle incidence resolution spectrometry. It was revealed that, driven by the formation of intermolecular hydrogen bonds, the molecular orientation changes from tilted edge-on to face-on orientation. In situ 2D-GIXD measurements confirmed that the change of molecular orientation is simultaneously caused by the cleaving of the Boc substituents. Time-resolved microwave conductivity measurements were used to show that the resulting NDI-H film has anisotropic charge-carrier transport with preferential mobility in the direction perpendicular to the film plane. We fabricated perovskite solar cells to demonstrate that the NDI-H film effectively functions as the bottom electron-transporting layer in these devices