Synthesis and Characterization of functional ceramic materials at the nano- and microscale with enhanced properties

Semiconductor nanoparticles (NPs) and nanowires (NWs) of doped ZnO system have been synthesised at low temperature (190 °C) by a novel Polyol-Mediated Thermolysis (PMT) process and Vapour-Solid (VS) reaction. Ce/Ru doped ZnO NPs with different molar content (1-3--5-10%) have been synthesised by both experimental processes. The crystallite size, morphology, specific surface area and band gap have been evaluated. Also, the structural and functional characteristics were carried out by X-ray diffraction technique (XRD), high resolution transmission electron microscopy (HRTEM), Brunauer, Emmett and Teller (BET) method, UV-Vis diffuse reflectance spectra (DRS), UV-Vis spectroscopy and photoluminescence measurements (PL). Also, the photocatalytic activities of ZnO nanoparticles were evaluated by removal rate of methyleneblue (MB) under UV irradiation (365 nm) at RT. XRD patterns revealed a hexagonal ZnO wurtzite-type crystalline structure with a preferred orientation of(101) plane. Any secondary phases have been identified such as Ce02, Ce203, ee, Ru02, Ru304, Ru. HRTEM showed NPs in shape from spherical/ellipsoidal to hexagonal, that does not change significantly with the increasing of precursor solution concentration and kind of dopant element in the samples obtained from PMTprocess. The size of NPs was observed in the range from 16 to 23 run. Using the Kubelka-Munk treatment on the diffuse reflectance spectra, the direct band energy has been estimated at