Elaboration of ceramic composites with low thermal expansion coefficient for space applications

Actuellement, la qualité de l’imagerie provenant de systèmes optiques spatiaux est limitée par la taille de leurs miroirs et la masse des structures supportant le miroir. Le développement de systèmes athermiques légers (un seul matériau) constitue le principal challenge dans l’amélioration de ces systèmes. De matériaux légers, résistants mécaniquement (E/ρ3 > 10, σf > 100 MPa) et stables thermiquement ( 10, σf > 100 MPa) and thermal stability (< 2.0e-6/K) are required. Within this context, our project consists in processing new ceramic composites by combining positive thermal expansion coefficient (TEC) materials having good mechanical properties (alumina or ceria doped zirconia) and negative TEC materials (zirconium tungstate or β-eucryptite) The processing of zirconium tungstate-based materials showed several decomposition and chemical reactions with some oxide matrix leading to its giving up. In the case of β-eucryptite, vermicular phenomenon occurs during sintering leading to the formation of intragranular porosity. Sintering parameters optimization can limit this porosity. The study of the thermal behavior of pure β-eucryptite materials shows that the very negative TEC results from microcracking, generated by the TEC anisotropy of its crystal lattice. This microcracking depends on the grain size and the aggregate size in the case of powder materials. Despite the fact that the TEC of its lattice (called intrinsic TE C equals to -0.4e-6/K) is very low, its bulk (or extrinsic) TEC can reach values until -10.9e-6/K according to the processing conditions. In this work, two strategies for developing composites were studied. The first one consists in decreasing the matrix TEC using an uncracked β-eucryptite powder (-0.4e-6/K) while the second one consists in elaborating near zero TEC materials from a microcracked β-eucryptite powder (-3.0e-6/K). When ceria-doped zirconia is used, ceria content must be adjusted in order to limit zirconia phase transformation. This transformation is driven by tensile stresses induced by the β-eucryptite and modifies the composite thermal behavior linearity. In both studied cases, dense composites show a modification of the β-eucryptite intrinsic TEC from -0.4e-6/K to more than +3.2e-6/K as a consequence of compressive stresses applied by the oxide matrix. An uncompleted densification of composites is required to relax these stresses. Taking into account these observations, several very low TEC composites were elaborated. However, the uncompleted densification of composites and the β-eucryptite microcracking greatly decrease the mechanical properties of these materials