Silicon-rich SiO2/SiO2 multilayers: A promising material for the third generation of solar cell

International audienceSi-rich-SiO 2 SRSO / SiO 2 multilayers MLs have been grown by reactive magnetron sputtering. The presence of silicon nanoclusters Si-ncls within the SRSO sublayer and annealing temperature influence optical absorption as well as photoluminescence. The optimized annealing temperature has been found to be 1100 ° C, which allows the recovery of defects and thus enhances photoluminescence. Four MLs with Si-ncl size ranging from 1.5 to 8 nm have been annealed using the optimized conditions and then studied by transmission measurements. Optical absorption has been modeled so that a size effect in the linear absorption coefficient in cm −1 has been evidenced and correlated with TEM observations. It is demonstrated that amorphous Si-ncl absorption is fourfold higher than that of crystalline Si-ncls