Ethanol and Hydrogen Gas-Sensing Properties of CuO-CuFe2O4 Nanostructured Thin Films

Nanocrystalline CuO-CuFe2O4 composite thin films were developed from CuFeO2 ceramic target using a radio-frequency sputtering method followed by a thermal oxidation process. This fabrication process helps to develop porous sensing layers which are highly desirable for solid-state resistive gas sensors. Their sensing properties toward ethanol and hydrogen gas in dry air were examined at the operating temperatures ranging from 250 degrees C to 500 degrees C. The electrical transients during adsorption and desorption of the test gases were fitted with the Langmuir single site gas adsorption model. A composite thin film with a total thickness of 25 nm showed highest response (79%) toward hydrogen (500 ppm) at the operating temperature of 400 degrees C. The shortest response time (tau(res)) was found to he similar to 60 and similar to 90 s for hydrogen and ethanol, respectively. The dependence of the response of the sensor on gas concentration (10-500 ppm) was also studied