Corrosion inhibition of iron in 0.5 mol L-1 H2SO4 by halide ions

The inhibition effect of halide ions such as iodide, bromide and chloride ions on the corrosion of iron in 0.5 mol L-1 H2SO4 and the adsorption behaviour of these ions on the electrode surface have been studied by polarization and impedance methods. It has been found that the inhibition of nearly 90% has been observed for iodide ions at 2.5 <FONT FACE=Symbol>´</FONT> 10-3 mol L-1, for bromide ions at 10 <FONT FACE=Symbol>´</FONT> 10-3 mol L-1 and 80% for chloride ions at 2.5 <FONT FACE=Symbol>´</FONT> 10-3 mol L-1. The inhibition effect is increased with increase of halide ions concentration in the case of I- and Br- ions, whereas it has decreased in the case of Cl- ion at concentrations higher than 5 <FONT FACE=Symbol>´</FONT> 10-3 mol L-1. The double layer capacitance values have decreased considerably in the presence of halide ions which indicate that these anions are adsorbed on iron at the corrosion potential.O efeito de inibição de íons haletos, tais como iodeto, brometo e cloreto, na corrosão de ferro em solução 0,5 mol L-1 de H2SO4, e o comportamento da adsorção desses íons na superfície do eletrodo, foram estudados pelos métodos de polarização e de impedância. Foi observada uma inibição de aproximadamente 90% para íons iodeto a 2,5 <FONT FACE=Symbol>´</FONT> 10-3 mol L-1 e para íons brometo a 10 <FONT FACE=Symbol>´</FONT> 10-3 mol L-1, e de 80% para íons cloreto a 2,5 <FONT FACE=Symbol>´</FONT> 10-3 mol L-1. O efeito da inibição aumenta com o aumento da concentração dos íons haletos I- e Br-, mas decresce no caso do Cl-, para concentrações maiores que 5 <FONT FACE=Symbol>´</FONT>10-3 mol L-1. Os valores de capacitância de dupla camada diminuíram consideravelmente na presença dos íons haletos, o que indicou que esses ânions são adsorvidos no ferro no potencial de corrosão