Influence of chemical and mechanical polishing on water sorption and solubility of denture base acrylic resins

Influence of polishing methods on water sorption and solubility of denture base acrylic resins was studied. Eighty samples were divided into groups: Clássico (CL), and QC 20 (QC) - hot water bath cured; Acron MC (AC), and Onda Cryl (ON) - microwave cured; and submitted to mechanical polishing (MP) - pumice slurry, chalk powder, soft brush and felt cone in a bench vise; or chemical polishing (CP) - heated monomer fluid in a chemical polisher. The first desiccation process was followed by storage in distilled water at 37 ± 1ºC for 1 h, 1 day, 1, 2, 3 and 4 weeks. Concluding each period, water sorption was measured. After the fourth week, a second desiccation process was done to calculate solubility. Data were submitted to analysis of variance, followed by Tukey test (p<0.05). Means of water sorption (%) and solubility (%), respectively, were: CL-MP: 1.92 and 0.02; CL-CP: 1.98 and 0.52; QC-MP: 2.31 and -0.05; QC-CP: 2.32 and 0.25; AC-MP: 2.45 and -0.07; AC-CP: 2.43 and 0.41; ON-MP: 2.32 and -0.06; ON-CP: 2.34 and 0.27. Mechanical polishing promoted significantly lower solubility of acrylic resins; initially, water sorption values were higher for chemically polished samples, however, after 4 weeks all groups were similar.Este estudo avaliou a influência dos métodos de polimento na absorção de água e solubilidade da resina acrílica para base de prótese. Foram confeccionadas 80 amostras, divididas nos seguintes grupos: Clássico (CL), e QC 20 (QC) - polimerização por banho de água aquecida; Acron MC (AC), e Onda Cryl (ON) - polimerização por microondas; e submetidas ao polimento mecânico (PM) - pasta de pedra pomes, branco de Espanha, escova macia e cone de feltro em torno de bancada; ou polimento químico (PQ) - monômero específico em polidora química. O primeiro processo de dessecação foi seguido de armazenagem em água destilada a 37 ± 1ºC por 1 h, 1 dia, 1, 2, 3 e 4 semanas. Ao término de cada período, foi realizada mensuração da absorção de água. Após a quarta semana, um segundo processo de dessecação foi realizado para o cálculo da solubilidade. Os resultados foram submetidos à análise de variância e teste de Tukey (p