Electrosynthesized polyaniline for the corrosion protection of aluminum alloy 2024-T3

Adherent polyaniline films on aluminum alloy 2024-T3 have been prepared by electrodeposition from aniline containing oxalic acid solution. The most appropriate method to prepare protective films was a successive galvanostatic deposition of 500 seconds. With this type of film, the open circuit potential of the coating shifted around 0.065V vs. SCE compared to the uncoated alloy. The polyaniline coatings can be considered as candidates to protect copper-rich (3 - 5%) aluminum alloys by avoiding the galvanic couple between re-deposited copper on the surface and the bulk alloy. The performance of the polyaniline films was verified by immersion tests up to 2.5 months. It was good with formation of some aluminum oxides due to electrolyte permeation so, in order to optimize the performance a coating formulation would content an isolation topcoat.Filmes de polianilina aderentes a liga de alumínio 2024-T3 foram preparados por eletrodeposição a partir de soluções de ácido oxálico contendo anilina. O método mais apropriado para preparar filmes de proteção contra a corrosão foi uma deposição galvanostática sucessiva de 500 segundos. Com este tipo de filme, o potencial de circuito aberto do metal protegido deslocou de aproximadamente 0,065 V vs. ECS em comparação a liga não protegida. Coberturas de polianilina podem ser consideradas como candidatas para proteger ligas de alumínio com alto teor de cobre (3 - 5%) evitando o par galvânico entre o cobre redepositado na superfície e o seio da liga. A performance dos filmes de polianilina foi verificada com testes de imersão de até 2,5 meses. O resultado observado foi bom com a formação de alguns óxidos de alumínio devido a permeação de eletrólito e assim, para otimizar a performance de coberturas protetoras estas devem conter uma camada superior isolante