ESTUDO COMPARATIVO DA RESISTÊNCIA À FORÇA DE CISALHAMENTO DA RESINA COMPOSTA AO ESMALTE DENTAL CONDICIONADO COM ÁCIDO FOSFÓRICO OU LASER Nd: YAG

This study has been focused on a comparison between the shear bond strength of a composite resin attached to dental enamel surface, after a 35% phosphoric acid etching and after a Nd:YAG laser irradiation with 165.8 J/cm2 of energy density per pulse. After etching and attaching resin to these surfaces, the specimens were thermocycled and then underwent the shearing bond strength tests at a speed of 5 mm/min. The results achieved, after statistical analysis with Student's t-test, showed that the adhesion was significantly greater in the 35% phosphoric acid treated group than in the group treated with the Nd:YAG laser, thus demonstrating the need for developing new studies to reach the ideal parameters for an effective enamel surface conditioning as well as specific adhesives and composite resins when Nd:YAG laser is usedEste estudo foi conduzido a fim de comparar a resistência à força de cisalhamento de uma resina composta aderida à superfície do esmalte dental após condicionamento com ácido fosfórico a 35% ou com a irradiação de um laser Nd:YAG, com densidade de energia de 165,8 J/cm2 por pulso. Após o condicionamento e a adaptação da resina a essas superfícies, os espécimes sofreram ciclagem térmica e foram, então, submetidos ao teste de resistência à força de cisalhamento em uma velocidade de 5 mm/min. Os resultados encontrados, após análise estatística pelo teste t de Student, revelaram que a adesão foi significantemente maior no grupo tratado pelo ácido fosfórico a 35% do que no grupo tratado pelo laser Nd:YAG, revelando, dessa forma, a necessidade do desenvolvimento de novos estudos, a fim de se alcançarem os parâmetros ideais para o condicionamento da superfície do esmalte, bem como adesivos e resinas compostas específicas, quando o laser Nd:YAG é utilizad