Corrosion behavior of CuAlMn alloy in NaCl solution : diploma thesis

U radu je ispitano korozijsko ponašanje CuAlMn legure u 0,9 % otopini NaCl pri pH = 7,4, 5,4 i 3,4 te temperaturama elektrolita od 25, 37 i 50 o C u mirujućoj otopini. Također je ispitan i utjecaj miješanja otopine na korozijsko ponašanje CuAlMn legure. Elektrokemijska ispitivanja provedena su mjerenjem potencijala otvorenog strujnog kruga, metodom linearne i potenciodinamičke polarizacije. Nakon polarizacijskih mjerenja, površine elektroda ispitane su optičkim mikroskopom, a također je na njima napravljena i SEM/EDS analiza. Rezultati ispitivanja su pokazali da povećanjem koncentracije kloridnih iona dolazi do porasta gustoće korozijske struje i do sniženja vrijednosti polarizacijskog otpora, što ukazuje na intenzivniju koroziju CuAlMn legure. Mikroskopske snimke površine jasno ukazuju na negativan utjecaj gibanja elektrolita, povišenja temperature i smanjenja pH vrijednosti elektrolita na korozijsku otpornost CuAlMn legure, koji se očituje u vidu povećanja hrapavosti površine uslijed intenzivnije korozije. SEM snimke površine legure jasno pokazuju značajan utjecaj temperature na povećanje intenziteta korozijskih procesa. Tako pri 50 o C na površini CuAlMn legure jasno su vidljivi duboki kanali i šupljine nastale intenzivnim otapanjem legure. EDS analiza površine CuAlMn legure nakon potenciodinamičkog polarizacijskog mjerenja u 0,9 % NaCl otopini pri T = 37 o C i pH = 7,4, koje je prekinuto na potencijalu 0,463 V, utvrdila je prisustvo svih legirnih elemenata na površini. Daljnjim pozitiviranjem potencijala dolazi do uklanjanja legirnih elemenata Al i Mn s površine tako da je pri potencijalu od 1,5 V dominantan element na površini Cu.The corrosion behavior of CuAlMn alloy was investigated in 0.9 % NaCl solution at pH 7.4, 5.4 and 3.4 and at electrolyte temperatures of 25, 37 and 50 o C in stagnant solution. The effect of solution mixing on the corrosion behavior of CuAlMn alloys was also investigated. Electrochemical investigations were performed by measuring open circuit current potential, linear and potentiodynamic polarization. After polarization measurements, electrode surfaces were examined by optical microscope, and SEM/EDS analysis. The results of the investigations have shown that the increase of the chloride ions concentration increases the corrosion currents density and reduces the value of the polarization resistance, indicating a more intense corrosion of the CuAlMn alloy. Microscopic surface analysis clearly showed the negative impact of electrolyte motion, temperature elevation, and electrolyte pH decrease in corrosion resistance of CuAlMn alloy, which is manifested in increased surface roughness due to more intense corrosion. SEM Surface analysis clearly show a significant influence of temperature on increasing the intensity of corrosion processes. Thus, at 50 o C on the CuAlMn alloy surface, deep canals and cavities are formed by the intensive dissolution of the alloy. The EDS surface analysis after potentiodynamic polarization measurement in 0.9 % NaCl solution at T = 37 o C and pH = 7.4, interrupted at 0.463 V, determined the presence of all alloy elements on the surface. Further changes the potential in a positive direction lead to the removal of alloying elements Al and Mn from the surface so at the potential of a 1.5 V, Cu was a dominant element on the alloy surface