Oxidation behavior of a Mo (Si, Al)(2)-based composite at 300-1000 degrees C

The oxidation behavior of a Mo (Si,Al)(2)-based composite of Mo(Si,Al)(2), Al2O3 and Mo-5(Si,Al)(3) (Kanthal Super ER) in synthetic air was investigated. The samples were oxidized isothermally for up to 72 h at 300-1000 degrees C using a thermobalance. The microstructure was analyzed by X-ray diffraction (XRD), Scanning Electron Microscopy (SEM) and Auger Electron Spectroscopy (AES) depth profiling. Broad ion beam milling (BIB) was used to prepare cross-sections. Oxidation behavior depended strongly on the composition of the substrate which consisted of a Mo(Si,Al)(2) matrix and the minority phases Mo-5(Si,Al)(3) and Al2O3. At 300-500 degrees C the mass gains were small with parabolic kinetics, oxidation resulting in a mixture of oxides that reflects the substrate composition. At 600 and 700 degrees C the oxide scale is thin and protective and depleted in molybdenum, a mass loss occurring due to MoO3 vaporization. At 1000 degrees C a protective alpha-alumina scale forms