Use of sintering to immobilize toxic metals present in galvanic sludge into a stabile glass-ceramic structure

Galvanization process requires the use a large amount of water and produces wastewaters that are usually purified by conventional cost-effective procedure. This kind of treatment generates waste sludge which becomes a hazardous if is not properly stabilized. Hence, the aim of this paper is to investigate the characteristics of galvanic sludge through the inspection of its physicochemical parameters and consider stabilization of waste materials, including waste glass and aluminum slag by their conversion into an eco-designed material referred to as glass ceramics. The obtained products have been studied by X-ray diffraction (XRD). XRD analyses confirmed occurrence of chemical and phase transformations in treated galvanic sludge and binding of toxic metals (Al3+, Cr3+, Cu2+, Cd2+, Ni2+, Pb2+, Zn2+) into crystalline phases and very sTab. structure.Процес галванизације захтева велику количину технолошке воде што има за последицу стварање отпадних вода, које се из економских разлога пречишћавају конвенционалним системима. Овим третманом настаје отпадни муљ који, уколико се адекватно не стабилизује, представља опасан отпад. У том смислу, у раду је извршена карактеризација галванског муља анализом физичкохемијских параметара компонената, а затим стабилизација ових отпадних материја, укључујући отпадно стакло и алуминијумску шљаку, превођењем у еко-синтеровани материјал стаклокерамика. Добијени производ анализиран је рендгенском дифракционом анализом (XRD). На основу XRD спектра потврђене су хемијско-фазне трансформације третираног галванског муља и везивање токсичних метала (Al3+, Cr3+, Cu2+, Cd2+, Ni2+, Pb2+, Zn2+) у веома стабилну кристалну структуру