Development of electrochemical method for assessment of the quality of hot dip galvanizing on threaded metallic construction elements

U ovom radu analizirane su površine vruće pocinčanih vijaka kako bi se ispitala mogućnost primjene elektrokemijskih tehnika za ocjenu kvalitete vrućeg pocinčanja na elementima s navojima. Analizirane su tri grupe vijaka: novi nekorišteni vijci, vijci skladišteni tijekom tri mjeseca na otvorenom i korišteni vijci koji su skinuti s konstrukcije godinu dana nakon montaţe. Za usporedbu analizirani su i novi elektrolitički pocinčani vijci. Uzorci su podvrgnuti mikroskopskim analizama, mjerenju debljine i hrapavosti prevlake, te elektrokemijskim mjerenjima potencijala površine, potencijala otvorenog kruga, polarizacijskog otpora i elektrokemijske impedancijske spektroskopije. Kombinacijom elektrokemijskih i neelektrokemijskih metoda pokazano je da izlaganje sve oštrijim uvjetima okoliša uzrokuje pad debljine sloja cinka na vijcima, pad potencijala površine vijaka, pad potencijala otvorenog kruga i pad hrapavosti. Polarizacijski otpor, kao i otpori dobiveni iz impedancijskih mjerenja ne pokazuju korelaciju s uvjetima izlaganja vijaka, ali pokazuju odnos izmeĎu korozijske aktivnosti površine cinka i korozijskih procesa u porama zaštitnog sloja.In this paper the surface of hot dip galvanized bolts was analyzed to examine the possibility of application of electrochemical techniques for evaluating the quality of hot dip galvanizing on threaded elements. Three groups of bolts were analized: new unused bolts, bolts stored outdoor during three months and used bolts removed from construction one year after assembly. For comparison, new electrolitically galvanized bolts were also analyzed. Samples were submitted to microscopic analysis, measurement of zinc layer thickness and roughness and electrochemical measurements in order to determine surface condition and provide information of corrosion resistance of zinc coating. By combining electrochemical and other methods it was shown that exposure to increasingly severe environmental conditions causes a drop in: zinc layer thicknes, surface potential, open circuit potential and surface roughness. Polarization resistance and the resistances obtained from impedance measurements are not in correlation with the conditions of exposure of screws, but show the relationship between the corrosion activity of zinc surface and corrosion processes in the pores of zinc coating