The characteristics of martensitic transformation is strongly dependent on the cooling rate applied to the material. For a quenched and tempered steel, the martensitic transformation occurs below 500 °C, but in industry, cooling rates are normally characterized for cooling in the temperature regime between 800 and 500 °C. The effects of different cooling rates in the lower temperature regime were thus, not intensively investigated in the past. To this end, a 50CrMo4 steel is quenched in a dilatometer applying varying cooling rates below 500 °C. The martensite microstructure is analyzed by APT, TEM and EBSD in regard to carbon distribution, lath width and block sizes. Additionally, hardness measurements are carried out and martensite start t...
The 9Cr-1Mo ferritic-martensitic ODS steel is a promising structural material for the next generatio...
The current work contains experimental and theoretical work about the formation of martensite from t...
The current work contains experimental and theoretical work about the formation of martensite from t...
The characteristics of martensitic transformation is strongly dependent on the cooling rate applied ...
International audienceThe influence of cooling rate below the martensite start temperature, Ms, on t...
International audienceThe influence of cooling rate below the martensite start temperature, Ms, on t...
International audienceThe influence of cooling rate below the martensite start temperature, Ms, on t...
The aim of the performed experiments was to determine the influence of a cooling rate on the evoluti...
The aim of the performed experiments was to determine the influence of a cooling rate on the evoluti...
The aim of the performed experiments was to determine the influence of deformation and of austenitiz...
The aim of the performed experiments was to determine the influence of deformation and of austenitiz...
The cooling rate, density of stacking faults, austenite grain size, and temperature strongly influen...
International audienceLow-alloy 16 to 20MND5 steels are used for the production of nuclear reactor c...
International audienceLow-alloy 16 to 20MND5 steels are used for the production of nuclear reactor c...
International audienceLow-alloy 16 to 20MND5 steels are used for the production of nuclear reactor c...
The 9Cr-1Mo ferritic-martensitic ODS steel is a promising structural material for the next generatio...
The current work contains experimental and theoretical work about the formation of martensite from t...
The current work contains experimental and theoretical work about the formation of martensite from t...
The characteristics of martensitic transformation is strongly dependent on the cooling rate applied ...
International audienceThe influence of cooling rate below the martensite start temperature, Ms, on t...
International audienceThe influence of cooling rate below the martensite start temperature, Ms, on t...
International audienceThe influence of cooling rate below the martensite start temperature, Ms, on t...
The aim of the performed experiments was to determine the influence of a cooling rate on the evoluti...
The aim of the performed experiments was to determine the influence of a cooling rate on the evoluti...
The aim of the performed experiments was to determine the influence of deformation and of austenitiz...
The aim of the performed experiments was to determine the influence of deformation and of austenitiz...
The cooling rate, density of stacking faults, austenite grain size, and temperature strongly influen...
International audienceLow-alloy 16 to 20MND5 steels are used for the production of nuclear reactor c...
International audienceLow-alloy 16 to 20MND5 steels are used for the production of nuclear reactor c...
International audienceLow-alloy 16 to 20MND5 steels are used for the production of nuclear reactor c...
The 9Cr-1Mo ferritic-martensitic ODS steel is a promising structural material for the next generatio...
The current work contains experimental and theoretical work about the formation of martensite from t...
The current work contains experimental and theoretical work about the formation of martensite from t...