Thermomagnetic behavior and first order magnetization processes of Sm3Fe29-xTx and Sm3Fe29-xTxN4 (T = V and Cr)

A systematic investigation of structure and intrinsic magnetic properties of the compounds Sm3Fe29-xTx (T = V and Cr) and their nitrides has been performed. Nitrogenation resulted in remarkable improvements in the saturation magnetization and anisotropy fields at 4.2 K and room temperature. First order magnetization processes are observed at around 5.7 T for Sm3Fe26.7V2.3 and around 2.8 T for Sm3Fe24.0Cr5.0 and Sm3Fe24.0Cr5.0N4, respectively. The spin reorientation of the easy magnetization direction of Sm3Fe26.7V2.3 is observed at around 230 K. As a preliminary result, the maximum remanence B-r of 0.94 T, the coercivity mu(0)H(C) of 0.75 T, and the maximum energy product (BH) of 108.5 kJ/m(3) for the nitride magnet Sm3Fe26.7V2.3N4 are achieved by ball-milling at 293 K