Analysis of bending behavior of native and engineered auricular and costal cartilage

A large-deflection elasticity model was used to describe the mechanical behavior of cartilaginous tissues during three-point bending tests. Force-deflection curves were measured for 20-mm long x 4-mm wide x approximately 1-mm thick strips of porcine auricular and costal cartilage. Using a least-squares method with elastic modulus in bending as the only adjustable parameter, data were fit to a model based on the von Karman theory for large deflection of plates. This model described the data well, with an average RMS error of 14.8% and an average R(2) value of 0.98. Using this method, the bending modulus of auricular cartilage (4.6 MPa) was found to be statistically lower (p 0.05), reaching only about a third of the values of native samples