Add to ORKGTo assess the steel corrosion resistance for Calcium aluminate cement and Ordinary portland cement against internal chloride ions, mortar specimens were cast, assuming aggregates are inert. Linear polarisation, half-cell potential and mass loss were chosen to measure the rate of steel corrosion.��� ��������� ��������������� ������ ������������ ��������������������� ������ ������������ ������������ ������������������ ��� ��������������� ������ (10������������E02)������ ������������ ��������������
Up to this time all the methods to measure the corrosion rate of reinforcing steels embedded in hard...
In this stduy, Calcium aluminate cement (CAC) and Ordinarly portalnd cement (OPC) concretes were eva...
本研究係透過調整水膠比(0.35、0.45、0.55、0.65)，及數種卜作嵐材料添加率(飛灰取代水泥10%、20%、30%；爐石取代水泥15%、30%、50%)，以探討不同的配比對混凝土耐久性之影響...
The purpose of this study is development a free-cement. The Monitoring of galvanic current depending...
The influence of portland cement class on the corrosion rate of steel reinforcement ...
��� ��������� ��������� ������������ ��������� ��������������� ��������������� ������ ��������� ����...
To assess the resistance of steel against corrosion, mortar specimens were manufactured with a centr...
Concrete specimens with various binders including Portland cement, fly ash, blast furnace slag and c...
Calcium aluminate cement (CAC) is a binder whose hydrated compounds change over time from cubic phas...
This study is aimed to make calcium hydroxide on the cement steel interface which can improve buffer...
Mineral additions can eliminate the conversion in calcium aluminate hydrates and thus inhibit the fu...
Steel bars embedded in an alkali-activated slag (AAS) concrete were exposed (after curing for 28 day...
Steel embedded in concrete passivates due to the formation of an oxide film that may be broken by ex...
This study examines the corrosion of embedded steels in concrete or mortar using galvanic cell, half...
The long-term corrosion behaviour of reinforcing steel embedded in alkali-activated mortars (AAMs) p...
Up to this time all the methods to measure the corrosion rate of reinforcing steels embedded in hard...
In this stduy, Calcium aluminate cement (CAC) and Ordinarly portalnd cement (OPC) concretes were eva...
本研究係透過調整水膠比(0.35、0.45、0.55、0.65)，及數種卜作嵐材料添加率(飛灰取代水泥10%、20%、30%；爐石取代水泥15%、30%、50%)，以探討不同的配比對混凝土耐久性之影響...
The purpose of this study is development a free-cement. The Monitoring of galvanic current depending...
The influence of portland cement class on the corrosion rate of steel reinforcement ...
��� ��������� ��������� ������������ ��������� ��������������� ��������������� ������ ��������� ����...
To assess the resistance of steel against corrosion, mortar specimens were manufactured with a centr...
Concrete specimens with various binders including Portland cement, fly ash, blast furnace slag and c...
Calcium aluminate cement (CAC) is a binder whose hydrated compounds change over time from cubic phas...
This study is aimed to make calcium hydroxide on the cement steel interface which can improve buffer...
Mineral additions can eliminate the conversion in calcium aluminate hydrates and thus inhibit the fu...
Steel bars embedded in an alkali-activated slag (AAS) concrete were exposed (after curing for 28 day...
Steel embedded in concrete passivates due to the formation of an oxide film that may be broken by ex...
This study examines the corrosion of embedded steels in concrete or mortar using galvanic cell, half...
The long-term corrosion behaviour of reinforcing steel embedded in alkali-activated mortars (AAMs) p...
Up to this time all the methods to measure the corrosion rate of reinforcing steels embedded in hard...
In this stduy, Calcium aluminate cement (CAC) and Ordinarly portalnd cement (OPC) concretes were eva...
本研究係透過調整水膠比(0.35、0.45、0.55、0.65)，及數種卜作嵐材料添加率(飛灰取代水泥10%、20%、30%；爐石取代水泥15%、30%、50%)，以探討不同的配比對混凝土耐久性之影響...