The catalytic effect of Pt nanoparticles supported on silicon oxide nanowire

3.5 nm sized Pt nanocatalysts supported on silicon oxide nanowires (SiO(X)NWs) were fabricated by decorating the SiOXNWs with Pt nanoparticles using a simple physical deposition system without any surface pretreatment. High curvature of the nanowire surface together with the weak metal-substrate interaction helped to maintain discrete particle morphology with spherical shapes during deposition. Catalytic efficiency of the SiOXNWs coated with Pt nanoparticles was demonstrated through reduction of methylene blue in the presence of sodium borohydride. It was demonstrated that the highly curved nanowire surface allowed the Pt nanoparticles to be loaded with increased particle density, providing a larger surface area for the catalytic reaction. It was also shown that a simple heat treatment in vacuum improves the effectiveness of the Pt nanoparticles as a catalyst without loss of catalytic activity when used repeatedly. We expect that this metal nanoparticle-decorated nanowire can be easily extended to other heterogeneous reactions and can also be used as a template for building three-dimensional hierarchical nanostructures.This work was supported by the Ministry of Science and Technology through the Nanoscopia Center of Excellence at Hanyang University. This research was also partially supported by the Korea Research Foundation Grant funded by the Korean Government (MOEHRD) (KRF-2006-005-J04103)