Sintering Behavior of Columnar Thermal Barrier Coatings Deposited by Axial Suspension Plasma Spraying (SPS)

During the last decade, Suspension Plasma Spraying (SPS) attracted a lot of interest as an alternative process to produce columnar Thermal Barrier Coatings (TBCs). In this study, columnar TBCs were deposited with SPS. After spraying, samples were isothermally annealed at 1373 K for 1 h, 3 h, 10 h and 50 h, respectively. Microstructures and mechanical properties of the ceramic coatings were investigated as a function of annealing time. Annealing resulted in healing of micro-cracks, coarsening of pores, growth of domain size, companied with a decrease of porosity within columns. The change of coating microstructure led to change of mechanical properties. In addition, residual stress in SPS coatings was also investigated. Furthermore, as-sprayed coatings and pre-annealed coatings were subjected to burner rig tests. Short time pre-annealing allowed to enhance thermal cycling lifetime of such SPS coatings. The thermal cycling results were related to microstructure modifications of coatings