This paper focuses on the adherence during ageing of a primer (made of polyester resins crosslinked with melamine) applied onto hot-dip galvanized (HDG) steel for coil coating application and its influence on corrosion protection. A chromium-free surface treatment, composed of fluorotitanic acid, phosphoric acid, manganese phosphate, and vinylphenol was applied on the HDG steel to obtain high corrosion resistance and high adherence of a polyester and melamine primer. The influence of the manganese phosphate on the corrosion and adherence was investigated. To measure the adherence between the metal and the primer, a three-point flexure test was set up. The adherence was then linked with corrosion resistance during ageing, using electrochemic...
Since the use of hexavalent chromium in automotive and electronic equipment is largely prohibited, m...
De nos jours, la galvanisation continue par immersion à chaud est largement utilisée dans les struct...
The corrosion performance of electrogalvanised steel sheets pre-treated with a Cr3+ or Cr+6 -based c...
Conversion coatings are generally required to enhance organic coating adhesion and corrosion resista...
The corrosion performance of electrogalvanised steel sheets pre-treated with a Cr3+ or Cr+6-based co...
Investigations were carried out to assess the role of primer, pretreatments and coating microstructu...
The annealing galvanized steel (Galvanneal) is produced from hot-dip galvanized steel thermally trea...
Corrosion of steel in concrete is one of the major causes of structure degradation, requiring expens...
This article examines the resistance of corrosion-resistant polymeric materials to chemical reagents...
The adhesion and electrochemical properties of epoxy coatings electrodeposited on hot-dip galvanized...
This thesis investigates the development of coatings to be applied via a two-roll roller coating sys...
The main driving forces concerning the use of pre-primed automotive sheet are corrosion protection i...
The performance of different pre-treated galvanized steel/primer/topcoat paint systems applied on ho...
AbstractThe annealing galvanized steel (Galvanneal) is produced from hot-dip galvanized steel therma...
Nowadays continuous hot-dip galvanizing is widely used in metallic structures to protect steels agai...
Since the use of hexavalent chromium in automotive and electronic equipment is largely prohibited, m...
De nos jours, la galvanisation continue par immersion à chaud est largement utilisée dans les struct...
The corrosion performance of electrogalvanised steel sheets pre-treated with a Cr3+ or Cr+6 -based c...
Conversion coatings are generally required to enhance organic coating adhesion and corrosion resista...
The corrosion performance of electrogalvanised steel sheets pre-treated with a Cr3+ or Cr+6-based co...
Investigations were carried out to assess the role of primer, pretreatments and coating microstructu...
The annealing galvanized steel (Galvanneal) is produced from hot-dip galvanized steel thermally trea...
Corrosion of steel in concrete is one of the major causes of structure degradation, requiring expens...
This article examines the resistance of corrosion-resistant polymeric materials to chemical reagents...
The adhesion and electrochemical properties of epoxy coatings electrodeposited on hot-dip galvanized...
This thesis investigates the development of coatings to be applied via a two-roll roller coating sys...
The main driving forces concerning the use of pre-primed automotive sheet are corrosion protection i...
The performance of different pre-treated galvanized steel/primer/topcoat paint systems applied on ho...
AbstractThe annealing galvanized steel (Galvanneal) is produced from hot-dip galvanized steel therma...
Nowadays continuous hot-dip galvanizing is widely used in metallic structures to protect steels agai...
Since the use of hexavalent chromium in automotive and electronic equipment is largely prohibited, m...
De nos jours, la galvanisation continue par immersion à chaud est largement utilisée dans les struct...
The corrosion performance of electrogalvanised steel sheets pre-treated with a Cr3+ or Cr+6 -based c...