The effect of process control agents and milling atmosphere on the structural changes of Ti 50 Cu 27,5 Ni 10 Zr 10 Co 2,5 master alloy during short time milling

Properties of powders made from Ti 50 Cu 27,5 Ni 10 Zr 10 Co 2,5 alloy, milled under different conditions for only 3600 s in total were investigated. For this purpose two different milling atmospheres and two different Process Control Agents (PCA) were tested: argon without PCA, air without PCA, argon combined with stearic acid, argon combined with petroleum spirit. Results showed that the size and shape of particles, and the microstrucutre and hardness of partcicles were highly depended on the milling conditions. According to XRD analysis, the maximal amorphous fraction has been achieved in the air atmosphere withouth PCA milled sample (57 wt. %) powder. However the extent of Fe contamination and weight loss during milling powder resulted bigger values. As a result, the optimal combination of morphology, contamination amount and weight lost level has been observed in the case of powder milled in argon atmosphere using stearic acid