Synthesis, characterization and spectroscopic investigation of Cr3+ doped wollastonite nanophosphor

This work explores the preparation of nanocrystalline Cr3+ (1-5 mol%) doped CaSiO3 phosphors by solution combustion process and study of its photoluminescence (PL) behavior. The nanopowders are well characterized by powder X-ray diffraction (PXRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and Fourier transform infra-red (FTIR) spectroscopy. PXRD results confirm monoclinic phase upon calcination at 950 degrees C for 3 h. SEM micrographs indicates that the powder is highly porous and agglomerated. The TEM images show the powder to consist of spherical shaped particles of size similar to 30-60 nm. Upon 323 nm excitation, the emission profile of CaSiO3:Cr3+ exhibits a narrow red emission peak at 641 nm due to E-2 -> (4)A(2) transition and broad band at 722 nm due to T-4(2g) -> (4)A(2g). It is observed that PL intensity increases with increase in Cr3+ concentration and highest PL intensity is observed for 3 mol% doped sample. The PL intensity decreases with further increase in Cr3+ doping. This decrease in PL intensity beyond 3 mol% is ascribed to concentration quenching. Racah parameters are calculated to describe the effects of electron-electron repulsion within the crystal lattice. The parameters show 21% reduction in the Racah parameter of free ion and the complex, indicating the moderate nephelauxetic effect in the lattice. (C) 2014 Elsevier B.V. All rights reserved