Vliv vodíkového plazmatu na modelové korozní vzorky bronzu

Our work is about plasmachemical reduction of model corrosion layers. The model corrosion layers were produced on bronze samples with size of 10 x 10 x 5 mm3, containing Cu and Sn. Concentrated hydrochloric acid was used as a corrosive environment. The application of reduction process in low-pressure low-temperature hydrogen plasma followed. A quartz cylindrical reactor with two outer copper electrodes was used. Plasma discharge was generated in pure hydrogen by a RF generator. Each corroded sample was treated in different conditions (supplied power and a continual or pulsed regime with a variable duty cycle mode). Process monitoring was ensured by optical emission spectroscopy. After treatment, samples were analyzed by SEM and EDX.Práce je zaměřena na plazmochemickou redukci modelových korozních vrstev. Modelové korozní vrstvy byly připraveny na bronzových vzorcích o rozměrech 10 x 10 x 5 mm3. Jako korozní prostředí byly použity páry koncentrované kyseliny chlorovodíkové. Pro redukci byl použit křemenný válcový reaktor s vnějšími měděnými elektrodami, RF výboj byl generován v čistém vodíku. Každý korodovaný vzorek byl v plazmatu ošetřen za odlišných podmínek (výkon, střída), proces byl monitorován optickou emisní spektrometrií. Po opracování byly vzorky analyzovány pomocí SEM a EDX