Effect of alloy treatment and coiling temperature on microstructure and bending performance of ultra-high strength strip steel

Two different high strength B-containing microalloyed steel strips produced in industrial processing conditions, one treated with Ti and the other treated with Al, processed by controlled rolling, accelerated cooling and coiling in two different temperatures ranges [723 K to 733 K (450 °C to 460 °C)] and [633 K to 653 K (360 °C to 380 °C)] were subjected to bend testing. The Ti treated steel coiled at the higher temperature 733 K (460 °C) showed the best bending performance. The relatively softer (tensile strength of and even {112} in the sub-surface region as well as uniformity of through thickness texture of the rolled sheet improve the bendability. In the presence of crack initiators, like coarse and brittle TiN particles found in the Ti treated steel, a harder microstructure and the presence of Cube and Goss texture in the sub-surface layer, seen for the lower coiling temperature can cause local transgranular cleavage cracking. Finally the post-uniform elongation obtained from tensile testing and bendability follow a good correlation