Variation in mechanical properties with crystallinity of a La-based bulk metallic glass

The influence of crystallinity on the mechanical properties of a bulk La-based metallic glass was investigated. The degree of crystallization in the metallic glass was systematically altered by varying the annealing time above the glass transition temperature, $T_g$. The elastic modulus, E, of the nanocrystalline amorphous matrix composite was observed to increase abruptly at ~40% crystallinity, χ. The hardness, H, however increases only linearly with the increase in χ. Instrumented impact test results show a significant decrease, by ~90%, in impact toughness, γ with the introduction of a small percentage of crystallinity. This decrease in toughness was also associated with a distinct change in fracture morphology, from a ductile vein type fracture in the bulk glass to intergranular cleavage fracture in the crystalline material. Microscopic mechanisms responsible for the observed transitions in mechanical properties are discusse