Add to ORKGSuperconducting $YBa_2Cu_30_7$ thin films have been deposited by high pressure oxygen sputtering technique (HOST). The epitaxial films prepared on MgO substrates have been analysed using Rutherford Backscattering Spectroscopy (RBS) and Auger Electron Spectroscopy (AES). The films are found to be stoichiometric and homogeneous. Thickness uniformity and surface roughness of these films have also been analysed. The possible sputter mechanism in this method has been discussed
The residual surface resistance of a number of films of YBa{sub 2}Cu{sub 3}O{sub 7}, prepared by off...
The dependence of YBCO thin film properties on the deposition conditions was studied for different s...
The critical current densities (Jc) have been measured at 77K in high pressure oxygen sputtered thin...
Superconducting $YBa_2Cu_30_7$ thin films have been deposited by high pressure oxygen sputtering tec...
$YBa_2Cu_30_{7_X}$ films have been deposited on (100) MgO substrates by a high pressure oxygen sputt...
Superconducting thin films of YBa2Cu3O7- x have been prepared by d.c. sputtering deposition followed...
Using direct-current magnetron sputtering deposition, we have successfully prepared high-quality epi...
Two types of growth processes of Y-Ba-Cu-O thin films were investigated: three step processes involv...
Superconducting $YBa_2Cu_3O_{7-\delta}$ films were formed using a high pressure oxygen sputtering te...
Ion beam analyses have been used for characterization of superconducting Y1Ba2Cu3O7 - x thin films d...
The sputter deposition of YBa2Cu3O7-x in a de-diode was performed in pure oxygen medium and an optic...
An optical spectroscopic study of the plasma produced during rf sputtering of an YBa2Cu3O7-x target ...
Superconducting YBCO thin films have been grown in-situ by three ion beam co-deposition sputtering. ...
The fabrication of superconducting Y1Ba2Cu3O7-delta films by d.c. sputter deposition was investigate...
C-axis oriented epitaxial YBa2Cu3O7-δ thin films ( Tc of 88 K and Jc of 107A/cm2 at 77K) were deposi...
The residual surface resistance of a number of films of YBa{sub 2}Cu{sub 3}O{sub 7}, prepared by off...
The dependence of YBCO thin film properties on the deposition conditions was studied for different s...
The critical current densities (Jc) have been measured at 77K in high pressure oxygen sputtered thin...
Superconducting $YBa_2Cu_30_7$ thin films have been deposited by high pressure oxygen sputtering tec...
$YBa_2Cu_30_{7_X}$ films have been deposited on (100) MgO substrates by a high pressure oxygen sputt...
Superconducting thin films of YBa2Cu3O7- x have been prepared by d.c. sputtering deposition followed...
Using direct-current magnetron sputtering deposition, we have successfully prepared high-quality epi...
Two types of growth processes of Y-Ba-Cu-O thin films were investigated: three step processes involv...
Superconducting $YBa_2Cu_3O_{7-\delta}$ films were formed using a high pressure oxygen sputtering te...
Ion beam analyses have been used for characterization of superconducting Y1Ba2Cu3O7 - x thin films d...
The sputter deposition of YBa2Cu3O7-x in a de-diode was performed in pure oxygen medium and an optic...
An optical spectroscopic study of the plasma produced during rf sputtering of an YBa2Cu3O7-x target ...
Superconducting YBCO thin films have been grown in-situ by three ion beam co-deposition sputtering. ...
The fabrication of superconducting Y1Ba2Cu3O7-delta films by d.c. sputter deposition was investigate...
C-axis oriented epitaxial YBa2Cu3O7-δ thin films ( Tc of 88 K and Jc of 107A/cm2 at 77K) were deposi...
The residual surface resistance of a number of films of YBa{sub 2}Cu{sub 3}O{sub 7}, prepared by off...
The dependence of YBCO thin film properties on the deposition conditions was studied for different s...
The critical current densities (Jc) have been measured at 77K in high pressure oxygen sputtered thin...