Modeling the conductivity around the dimensionality-controlled metal-insulator transition in LaNiO3/LaAlO3 (100) superlattices

A dimensionality controlled metal insulator transition in epitaxial [LaNiO3 (d nm)/LaAlO3(2nm)]10 (100) superlattices (thereafter [d/2]10 SLs) is demonstrated for decreasing LaNiO3 single layer thickness from 4nm down to 1.2 nm. The [4/2]10 SL shows metallic behavior with positive resistivity temperature coefficient, while the [2/2]10 SL shows a metal-insulator transition with crossover from 3D to two-dimensional single-layer dimensionality. Strong localization appears for the [1.2/2]10 SL with the resistivity being dominated by two-dimensional variable range hopping with a localization length of about 0.035 nm