Multilayer-Forming Behavior of Cr Nitrides and Carbides for Thermoreactive Deposition

The effect of a nitride layer on the forming behavior of CrN and (Cr, Fe)7C3 multilayers for thermoreactive deposition (TRD) was investigated. Plasma nitriding followed by TRD (PN-TRD) produced a larger coating thickness than the case of direct TRD with no plasma nitriding. For PN-TRD, an Fe2-3N layer of 10 μm in thickness was produced on AISI 52100 steels using plasma nitriding, followed by TRD using a mixed powder composed of 30 wt % Cr, 2 wt % NH4Cl, and 68 wt % Al2O3. During TRD at 800 °C, a CrN layer of 2 μm in thickness was formed along with a thin layer of mixed carbide (Cr7C3) and nitride (CrN) on top. As the deposition temperature was increased to 950 °C, a new layer of Cr7C3 was formed underneath the outermost layer composed of mixed Cr7C3 and CrN. At 950 °C, a Cr-rich zone indicated a thickness of ~7 μm. As the deposition time increased to 3 h at 950 °C, a new layer of (Cr, Fe)7C3 was produced at the interface between the CrN formed at 800 °C and the base metal. This layer formed because of the abundant resources of Cr and C provided from the TRD powder and base metal, respectively. The multilayer and interface were concretely filled without the formation of voids as the TRD time increased to 6 h at 950 °C. The TRD process on a pre-nitrided layer was successfully applied to produce multilayers of CrN and Cr7C3