The corrosion mechanism of the sintered (Ce, Nd)-Fe-B magnets prepared by double main phase and single main phase approaches

The sintered (Ce, Nd)-Fe-B magnets were produced widely by Double Main Phase (DMP) method in China as the magnetic properties of the DMP magnets are superior to those of single main phase (SMP) magnets with the same nominal composition. In this work, the microstructure and corrosion mechanism of the sintered (Ce0.2Nd0.8)30FebalB (wt.%) magnets prepared by DMP and SMP method were studied in detail. Compared to SMP magnets, the DMP magnets have more positive corrosion potential, lower corrosion current density, larger electron transfer resistance, and lower mass loss of the free corrosion experiment in 0.5mol/l Na2SO4 aqueous solution. All of the results show that the DMP magnets have better corrosion resistance than SMP magnets. The back scattered electron images show that the crystalline grains of the DMP magnets are sphericity with a smooth surface while the SMP ones have plenty of edges and corners. Besides, the distribution of Ce/Nd is much more uneven in both magnetic phase and rare earth (Re)-rich phase of the DMP magnets than those of SMP magnets. After corrosion, DMP magnets show eroded magnetic phase and intact Re-rich phase, which indicate that galvanic corrosion of the Re-rich phase acting as the cathode appears