Irradiation Resistance in Al (x) CoCrFeNi High Entropy Alloys

The irradiation behavior of Al (x) CoCrFeNi (x = 0.1, 0.75, and 1.5) high entropy alloys was studied under 3 MeV Au-ions irradiation. The microstructural change and volume swelling due to irradiation were investigated using transmission electron microscopy and atomic force microscopy. The results showed that, with increasing the Al contents, the phase crystal structures of the as-cast samples evolved from face-centered cubic (FCC), to FCC + body-centered cubic (BCC), and BCC and irradiation-induced volume swelling increased. All alloys showed exceptional structural stability when irradiated up to over 50 displacement per atom at 298 K, and the irradiation-induced volume swellings in Al (x) CoCrFeNi HEAs were significantly lower than conventional nuclear materials under similar irradiation dosages.National High Technology Research and Development Program of China [2009AA03Z113]; National Science Foundation of China [51471025, 51210105006]; 111 Project [B07003]; Program for Changjiang Scholars and the Innovative Research Team of the UniversitySCI(E)EIARTICLEdrzhangy@ustb.edu.cn102340-23446