Polyamide-6-based composites reinforced with pristine or functionalized multi-walled carbon nanotubes produced using melt extrusion technique

Polyamide-6-based composites with pristine or functionalized multi-walled carbon nanotubes were produced using melt extrusion technique. After chemical functionalization, defect formation and attachment of carboxylic (-COOH) or amine (-NH2) groups on carbon nanotubes was confirmed from high-resolution transmission electron microscope and Fourier transform infra-red spectroscope studies. Carbon nanotubes incorporation promoted growth of -form crystals with enhanced thermal stability through increase in crystallization temperature from 162 to 192?. Dynamic mechanical thermal analysis (DMTA) indirectly pointed out to a homogeneous, uniform dispersion of nanotubes with reduction in free volume of the polymer, exhibiting a slight increase in glass transition temperature and a significant drop in coefficient of thermal expansion value. Composites containing 0.5wt% NH2-carbon nanotubes show increases in elastic modulus and tensile strength by approximate to 60 and 76%, respectively. Uniform dispersion and high interfacial strength was manifested by drop in strain to failure and lack of evidence of carbon nanotubes debonding from the matrix.http://gateway.webofknowledge.com/gateway/Gateway.cgi?GWVersion=2&SrcApp=PARTNER_APP&SrcAuth=LinksAMR&KeyUT=WOS:000334398700004&DestLinkType=FullRecord&DestApp=ALL_WOS&UsrCustomerID=8e1609b174ce4e31116a60747a720701Materials Science, CompositesSCI(E)EI7ARTICLEmiqureshi@ksu.edu.sa101197-12074