Radiation preparation of PVA-g-NIPAAm in a homogeneous system and its application in controlled release

Thermosensitive PVA-g-NIPAAm copolymers were prepared by graft copolymerization of N-isopropylacrylamide (NIPAAm) onto poly (vinyl alcohol) (PVA) in homogeneous system of dimethyl sulfoxide (DMSO) by 60Co-?? irradiation at room temperature. The factors of affecting the grafting yield, such as radiation dose, dose rate, acid concentration, were investigated. It was found that the grafting yield was increased with dose up to 30 kGy, but decreased slightly with dose rate from 61.2 to 50.1 Gy/min. The acid concentration also had influence on the grafting yield. Then the hydrogel of PVA-g-NIPAAm copolymer was made through a freezing-thawing process. The PVA-g-NIPAAm hydrogel exhibited obvious thermal sensitivity, which was observed from the differences of swelling behavior in water at different temperatures (below or above LCST). In addition, the release of Methylene Blue (MB) from this kind of hydrogel was studied. The release rate of MB from PVA-g-NIPAAm copolymer hydrogel at 48??C was faster than that at 15??C due to the shrinkage of the hydrogel at 48??C.EI1