Effect of gamma irradiation on ethylene-octene copolymers

Two ethylene-octene copolymers (POE) were irradiated with Co-60 gamma radiation and influence of irradiation atmosphere, absorbed dose and heat treatment of samples on the crosslinking were studied. Thermal properties and crystalline morphology of non-irradiated and irradiated POE were determined by using differential scanning calorimetry (DSC) and wide-angle X-ray diffraction (WAXS), respectively. The Charlesby-Pinner equation was used to describe the relationship between absorbed dose and sol fraction. The gel fraction of irradiated POE was lower and decreased with the increase of octene content when irradiated in oxygen, compared to irradiation in nitrogen atmosphere. The gel fraction increased significantly with the increasing of absorbed dose for the two copolymers. Heat treatment of samples prohibited the crosslinking of irradiated POE. The DSC results indicated that a subtle change of thermal properties of POE was observed before and after gamma irradiation at low dose. No change was found from the WAXS spectra of non-irradiated and irradiated POE. For heat-treating samples, the Charlesby-Pinner equation can not fit perfectly with the relationship between the sol fraction and absorbed dose, but it fits well with the crosslinking reaction of POE pellets. (C) 2002 Elsevier Science Ltd. All rights reserved.Chemistry, PhysicalNuclear Science & TechnologyPhysics, Atomic, Molecular & ChemicalSCI(E)EICPCI-S(ISTP)1