Monitoring crack movement in polymer-based self-healing concrete through digital image correlation, acoustic emission analysis and SEM in-situ loading

A study was performed to assess the fitness of continuous monitoring methods to detect failure due to excessive strain on polymers bridging moving cracks in the context of self-healing concrete. Testing of several polymer precursors with distinct properties also allowed conclusions regarding the requirements for polymers in this application. Acoustic emission (AE) analysis was performed in parallel with digital image correlation (DIC) at the macro-scale. In addition, a micro-scale study was performed with tensile tests inside an SEM chamber. Detection of failure through AE analysis coupled with DIC was possible only in case of failure due to brittle fracture of a rigid foam after 9% strain, which generated high-energy acoustic events. Direct observation of interfaces with SEM insitu loading allowed determination of failure of a rigid foam due to cracking of the polymer matrix and detachment at the interface with the cementitious matrix, with an onset at 5% strain and complete detachment at 16% strain. For a flexible, continuous film of polymer, detachment occurred before 50% strain. Assuming adequate adhesion, polymers with high elongation (>100%) and modulus of elasticity much lower than 10 MPa are required if cracks subjected to a realistic amplitude of movement are targeted. (C) 2016 Elsevier Ltd. All rights reserved