Synthesis of bulk, dense, nanocrystalline yttrium aluminum garnet from amorphous powders

Amorphous powders of Al2O3x2014;37.5 mol% Y2O3 (yttrium aluminum garnet (YAG)) were prepared by coprecipitation, decomposed at 800xB0;C, and hot-pressed uniaxally at low temperature (600xB0;C) and a moderate pressure (750 MPa). Optimum conditions yielded microstructures with only 2% porosity and partial crystallization of YAG. Further processing using high quasi-hydrostatic pressure (1 GPa) at 1000xB0;C enabled the production of fully crystallized YAG with gt;96% relative density and a nanocrystalline grain size of x223C;70 nm. 13