Sintesis Hidroksiapatit melalui Precipitated Calcium Carbonate (PCC) Cangkang Kerang Darah dengan Metode Hidrotermal pada Variasi PH dan Waktu Reaksi

Hydroxyapatite Ca10(PO4)6(OH)2 is a calcium phosphate compound which is a bioactive ceramic material with high bioafinitas, used as bone implants, adsorbents and catalysts. Synthesis of hydroxyapatite can be made by using material which is rich of CaCO3 like PCC blood calm shell with a composition of 95.5% CaCO3. In this research, PCC blood calm shell which has calcium source was synthesized to HAp by hydrothermal process. pH of the reaction (10, 11, 12) and time reaction (22,24,26 hours) was be varied. The outcome of synthesis was characterized by using FTIR, XRD, SEM. The results of FTIR analysis, synthesis of HAp with hydrothermal method showed the formation of hydroxyapatite in the presence of peaks PO43- dan OH-. The highest peak is obtained at pH 10,11,12 at time reaction of 26 hours. XRD diffraction results in hydroxyapatite get the highest crystallinity at pH 12 at time reaction 26 hours with a hexagonal crystal structure and produce a more pure hydroxyapatite. SEM results showed morphology with clots and irregular round shape