Crystallization kinetics of narrow molecular weight distribution metallocene short-chain-branched polyethylene

Isothermal and non-isothermal crystallization kinetics of three metallocene-catalysed short-chain-branched polyethylene (SCBPE) fractions with different degree of branching were investigated by using differential scanning calorimetry (DSC). Narrow molecular weight fractions (M-w = 20,000 and M-w/M-n < 1.15) are used and the degree of branching (CH3 per 1000C) are 1.6, 10.4, 40 respectively. The regime I - II transition temperature are 119.8<degrees>C, 115.9 degreesC, 113.3 degreesC with the decreasing of degree of branching. Increasing the branch content decreases the rate of secondary nucleation, i,relative to the rate of surface spreading and so increases the range of supercooling over which regime I exists. The rate of bulk crystallization for both isothermal and non-isothermal crystallization decreases with the increasing of degree of branching. Both Ozawa Equation and Kissinger Equation are invalid for non-isothermal crystallization kinetics of SCBPE fractions,that means the effects of the branched chain on crystallization process are more complex than expected