Influence of the applied stress rate on the stress corrosion cracking of 4340 and 3.5NiCrMoV steels under conditions of cathodic hydrogen charging

Stress corrosion cracking (SCC) of as-quenched 4340 and 3.5NiCrMoV steels was studied under hydrogen charging conditions, with a cathodic current applied to the gauge length of specimens subjected to Linearly Increasing Stress Test (LIST) in 0.5M HSO solution containing 2g/l arsenic trioxide (AsO) at 30°C. Applied stress rates were varied from 20.8 to 6×10MPas. Both the fracture and threshold stress decreased with decreasing applied stress rate and were substantially lower than corresponding values measured in distilled water at 30°C at the open circuit potential. The threshold stress values correspond to 0.03-0.08 σ for 4340 and 0.03-0.2 σ for the 3.5NiCrMoV steel. SCC velocities, at the same applied stress rate, were an order of magnitude greater than those in distilled water. However, the plots of the crack velocity versus applied stress rate had similar slopes, suggesting the same rate-limiting step. The fracture surface morphology was mostly intergranular, with quasi-cleavage features