The influence of ceramic particles on bond strength of cold spray composite coatings on AZ91 alloy substrate

Al-AlO composite coatings were produced on AZ91D magnesium alloy substrates using kinetic metallization (KM), which is a special type of cold spray using a convergent barrel nozzle to attain sonic velocity. The effect of the volume fraction of AlO particles and KM spray temperatures on the microstructure, hardness of the composite coatings, the deposition efficiency, and the bond strength between the coating and substrate was studied. Results show that addition of AlO particles not only significantly improves the density of the coating, but also enhances the deposition efficiency to an optimum value. The bond strength of the composite coatings with the substrate was found to be much stronger than the coating itself, measured using a specially designed lug shear method. Furthermore, based on bond strength data and SEM analysis, higher AlO content resulted in a failure mode transition from adhesive failure to cohesive failure. This is considered a result of a competition between the strengthening of the ceramic reinforcing particles at the coating/substrate interface, and the weakening of coating cohesive strength due to an increase in the proportion of weaker Al-AlO bonds compared with stronger Al-Al bonds. Characterisation of the composite coating in terms of hardness, porosity and microstructure was also conducted